| Batch ID |
-
Batch ID:
05-2-2024 09:06 LERK
-
procedure:
-
general:
-
Operator Initials:
LERK
-
Mix Date and Time:
2024-02-05 09:06:28
-
Polymerization Date and Time:
2024-02-05 09:06:28
-
Resin Storage Temperature (°C):
null
-
Resin Storage atmosphere:
null
-
Resin Storage location:
null
-
Polymer Storage Temperature (°C):
23.2
-
Polymer Storage armosphere:
N2
-
Polymer Storage location:
Oven
-
Mixing Conditions:
null
-
Mixing Type:
Sonication
-
Mixing Time (min):
null
-
Preparation temperature (°C):
null
-
Use Glovebox:
null
-
Polymerization:
null
-
Type of polymerization:
FROMP
-
Ambient temperature (°C):
null
-
Resin temperaure at the start of polymerization (°C):
25
-
Select Geometry from geometries tab:
null
-
Geometry - Select from library:
MOLD-1
-
Resin Width (mm):
101.6
-
Total width (mm):
90
-
Resin height (mm):
70
-
Total height (mm):
76.2
-
Thickness (mm):
4.2
-
Empty-dim:
null
-
Initiation:
null
-
Initiation method:
THERMAL
-
Photocontrol:
null
-
Photocontrol?:
NO
-
null:
null
-
thermal initiation:
-
Heat Source:
RESISTIVE WIRE
-
Heat Source Name:
24-gauge Kanthal wire
-
Heater diameter (mm):
0.5
-
Submerged length (mm):
null
-
Power (W):
null
-
Voltage (V):
6.31
-
Current (A):
3.8
-
Heat source temperature (°C):
null
-
Induction time (s):
null
-
inputs:
-
monomers:
-
monomer-inputs:
-
-
name:
COD
-
SMILES:
C1/C=C\CC/C=C\C1
-
Measured mass (g):
25.5789
-
Measured volume (μL):
-
-
Computed mass (g):
25.5789
-
Molecular Weight:
108.18
-
Moles:
2.36e-01
-
Monomer mol%:
97.25
-
-
name:
ENB
-
SMILES:
CC=C1CC2CC1C=C2
-
Measured mass (g):
0.8037
-
Measured volume (μL):
null
-
Computed mass (g):
0.8037
-
Molecular Weight:
120.2
-
Moles:
6.69e-03
-
Monomer mol%:
2.75
-
monomer-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
catalysts:
-
catalyst-inputs:
-
-
name:
GC-2
-
SMILES:
CC1=CC(=C(C(=C1)C)N2CCN(C2=[Ru](=CC3=CC=CC=C3)(Cl)Cl)C4=C(C=C(C=C4C)C)C)C.C1CCC(CC1)P(C2CCCCC2)C3CCCCC3
-
Measured mass (mg):
38.4
-
Computed mass (g):
0.0384
-
Molecular Weight:
848.98
-
Moles:
4.52e-05
-
Monomer:Catalyst molar ratio:
5375.41
-
catalyst-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
inhibitors:
-
inhibitor-inputs:
-
-
name:
TBP
-
SMILES:
CCCCOP(=O)(OCCCC)OCCCC
-
Measured volume (μL):
24.9
-
Density:
0.925
-
Computed mass (mg):
0.0230325
-
Molecular Weight:
250.3
-
Moles:
9.20e-05
-
Inhibitor:Catalyst molar ratio:
2.03
-
inhibitor-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
additives:
-
additive-inputs:
-
additive-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
solvents:
-
solvent-inputs:
-
solvent-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
FROMP Measurements:
-
Measured frontal velocity (mm/s):
null
-
Measured frontal velocity with light exposure (mm/s):
null
-
Measured maximum temperature (°C):
null
-
Type of front:
SPIN
|
Extracted by
https://re-mat.clowder.ncsa.illinois.edu/api/extractors/remat.experiment.from_excel
on Jul 31, 2024
|
|