| Batch ID |
-
Batch ID:
00-1-1900 00:00 LDM
-
procedure:
-
general:
-
Operator Initials:
LDM
-
Mix Date and Time:
null
-
Polymerization Date and Time:
null
-
Resin Storage Temperature (°C):
20
-
Resin Storage atmosphere:
50
-
Resin Storage location:
Oven
-
Polymer Storage Temperature (°C):
null
-
Polymer Storage armosphere:
null
-
Polymer Storage location:
null
-
Mixing Conditions:
null
-
Mixing Type:
Sonication
-
Mixing Time (min):
5
-
Preparation temperature (°C):
25
-
Use Glovebox:
NO
-
Polymerization:
null
-
Type of polymerization:
NONE
-
Ambient temperature (°C):
null
-
Resin temperaure at the start of polymerization (°C):
null
-
Select Geometry from geometries tab:
null
-
Geometry - Select from library:
TUBE-1
-
Resin height (mm):
1
-
Diameter (mm):
2
-
Thickness (mm):
3
-
Tube length (mm):
1
-
Empty-dim:
null
-
Initiation:
null
-
Initiation method:
THERMAL
-
Photocontrol:
null
-
Photocontrol?:
NO
-
null:
null
-
thermal initiation:
-
Heat Source:
SOLDERING IRON
-
Heat Source Name:
null
-
Heater diameter (mm):
30
-
Submerged length (mm):
null
-
Power (W):
2
-
Voltage (V):
1
-
Current (A):
2
-
Heat source temperature (°C):
null
-
Induction time (s):
null
-
inputs:
-
monomers:
-
monomer-inputs:
-
monomer-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
catalysts:
-
catalyst-inputs:
-
catalyst-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
Sonication
-
Mixing time (mins):
null
-
inhibitors:
-
inhibitor-inputs:
-
inhibitor-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
additives:
-
additive-inputs:
-
-
name:
Fumed Silica (A200)
-
SMILES:
O=[Si]=O
-
Measured mass (g):
100
-
Measured volume (μL):
null
-
Computed mass (g):
100
-
Molecular Weight:
60.08
-
Moles:
1.66e+00
-
Wt Percent of Additives:
100.0
-
additive-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
solvents:
-
solvent-inputs:
-
solvent-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
|
Extracted by
https://re-mat.clowder.ncsa.illinois.edu/api/extractors/remat.experiment.from_excel
on May 4, 2025
|
|
| procedure |
-
procedure:
-
Experiment Type:
LMD_DCPD_POST_CURE
-
Sample Name:
DCPD:ENB_2500-1-8_postcure_1
-
Sample Mass (mg):
7.490 mg
-
Reference Pan Type:
Tzero Aluminum Hermetic
-
Run Date:
6/29/2023 10:23:06 PM
-
Operator:
JJL
-
Instrument Name:
DSC2A-01089
-
Instrument Type:
DSC250
-
Serial Number:
DSC2A-01089
-
Location of Instrument:
Manufacturing Test
-
Trios version:
5.0.0.44608
-
Ramp rate (°C/min):
10.0
-
Ramp Min Temp (°C):
-20.0
-
Ramp Max Temp (°C):
250.0
-
Analysis:
-
Max Heat Flow:
1.84
-
Min Baseline Temp:
109.358
-
Max Baseline Temp:
159.477
-
Glass transition temperature:
136.858
|
Extracted by
https://re-mat.clowder.ncsa.illinois.edu/api/extractors/remat.batch.parameters.from_txt
on May 4, 2025
|
|
| procedure |
-
procedure:
-
Experiment Type:
LMD_DCPD_POST_CURE
-
Sample Name:
DCPD:ENB_2500-1-8_postcure_1
-
Sample Mass (mg):
7.490 mg
-
Reference Pan Type:
Tzero Aluminum Hermetic
-
Run Date:
6/29/2023 10:23:06 PM
-
Operator:
JJL
-
Instrument Name:
DSC2A-01089
-
Instrument Type:
DSC250
-
Serial Number:
DSC2A-01089
-
Location of Instrument:
Manufacturing Test
-
Trios version:
5.0.0.44608
-
Ramp rate (°C/min):
10.0
-
Ramp Min Temp (°C):
-20.0
-
Ramp Max Temp (°C):
250.0
-
Analysis:
-
Max Heat Flow:
1.84
-
Min Baseline Temp:
109.358
-
Max Baseline Temp:
159.477
-
Glass transition temperature:
136.858
|
Extracted by
https://re-mat.clowder.ncsa.illinois.edu/api/extractors/remat.parameters.from_txt
on May 4, 2025
|
|