| Batch ID |
-
Batch ID:
10-3-2025 09:20 RHB
-
procedure:
-
general:
-
Operator Initials:
RHB
-
Mix Date and Time:
2025-03-10 09:20:16
-
Polymerization Date and Time:
2025-03-10 09:20:16
-
Resin Storage Temperature (°C):
null
-
Resin Storage atmosphere:
null
-
Resin Storage location:
null
-
Polymer Storage Temperature (°C):
null
-
Polymer Storage armosphere:
null
-
Polymer Storage location:
null
-
Mixing Conditions:
null
-
Mixing Type:
Sonication
-
Mixing Time (min):
null
-
Preparation temperature (°C):
null
-
Use Glovebox:
NO
-
Polymerization:
null
-
Type of polymerization:
FROMP
-
Ambient temperature (°C):
null
-
Resin temperaure at the start of polymerization (°C):
null
-
Select Geometry from geometries tab:
null
-
Geometry - Select from library:
SNL-1
-
Channel Length (mm):
36.57
-
Channel Width (mm):
9.74
-
Channel thickness (mm):
0.52
-
Photo Window y-location (mm):
77.96
-
Photo Window y-dimension (mm):
null
-
Empty-dim:
null
-
Initiation:
null
-
Initiation method:
THERMAL
-
Photocontrol:
null
-
Photocontrol?:
YES
-
null:
null
-
thermal initiation:
-
Heat Source:
SOLDERING IRON
-
Heat Source Name:
null
-
Heater diameter (mm):
null
-
Submerged length (mm):
null
-
Power (W):
null
-
Voltage (V):
null
-
Current (A):
null
-
Heat source temperature (°C):
null
-
Induction time (s):
null
-
photo control:
-
In situ light :
YES
-
Preirradiation:
NO
-
Light wavelength (nm):
385
-
Light Intensity (mW/cm^2):
30
-
Exposure duration (s):
null
-
Exposure area (mm^2):
null
-
inputs:
-
monomers:
-
monomer-inputs:
-
-
name:
Ethylidene Norbornene (ENB)
-
SMILES:
CC=C1CC2CC1C=C2
-
Measured mass (g):
0.3
-
Measured volume (μL):
null
-
Computed mass (g):
0.3
-
Molecular Weight (g/mol):
120.2
-
Moles:
2.50e-03
-
Monomer mol%:
4.2
-
-
name:
Dicyclopentadiene (DCPD)
-
SMILES:
C1C=CC2C1C3CC2C=C3
-
Measured mass (g):
5.7
-
Measured volume (μL):
null
-
Computed mass (g):
5.7
-
Molecular Weight (g/mol):
132.2
-
Moles:
4.31e-02
-
Monomer mol%:
72.48
-
-
name:
OBNBD
-
SMILES:
CC1(O2)C=CC2C3=C1C=CC=C3
-
Measured mass (g):
2
-
Measured volume (μL):
null
-
Computed mass (g):
2
-
Molecular Weight (g/mol):
144.173
-
Moles:
1.39e-02
-
Monomer mol%:
23.32
-
monomer-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
catalysts:
-
catalyst-inputs:
-
-
name:
GC-2
-
SMILES:
CC1=CC(=C(C(=C1)C)N2CCN(C2=[Ru](=CC3=CC=CC=C3)(Cl)Cl)C4=C(C=C(C=C4C)C)C)C.C1CCC(CC1)P(C2CCCCC2)C3CCCCC3
-
Measured mass (mg):
24
-
Computed mass (g):
0.024
-
Molecular Weight (g/mol):
848.98
-
Moles:
2.83e-05
-
Monomer:Catalyst molar ratio:
2104.22
-
catalyst-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
Sonication
-
Mixing time (mins):
null
-
inhibitors:
-
inhibitor-inputs:
-
-
name:
TBP
-
SMILES:
CCCCOP(=O)(OCCCC)OCCCC
-
Measured volume (μL):
null
-
Density:
0.925
-
Computed mass (g):
0.0037
-
Molecular Weight (g/mol):
250.3
-
Moles:
1.48e-05
-
Inhibitor:Catalyst molar ratio:
0.52
-
inhibitor-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
additives:
-
additive-inputs:
-
-
name:
Anthracene
-
SMILES:
C12=CC=CC=C1C=C3C=CC=CC3=C2
-
Measured mass (g):
0.02
-
Measured volume (μL):
null
-
Computed mass (g):
0.02
-
Molecular Weight (g/mol):
178.23
-
Moles:
1.12e-04
-
Wt Percent of Additives:
0.25
-
-
name:
N-hydroxynaphthalimide triflate
-
SMILES:
O=C1N(C(C2=CC=CC3=CC=CC1=C23)=O)OS(=O)(C(F)(F)F)=O
-
Measured mass (g):
0.02
-
Measured volume (μL):
null
-
Computed mass (g):
0.02
-
Molecular Weight (g/mol):
345.25
-
Moles:
5.79e-05
-
Wt Percent of Additives:
0.25
-
additive-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
solvents:
-
solvent-inputs:
-
solvent-procedure:
-
Prepared in GloveBox?:
NO
-
Preparation temperature (°C):
null
-
Mixing type:
N/A
-
Mixing time (mins):
null
-
FROMP Measurements:
-
Measured frontal velocity (mm/s):
null
-
Measured frontal velocity with light exposure (mm/s):
null
-
Measured maximum temperature (°C):
null
-
Type of front:
LINEAR
|
Extracted by
https://re-mat.clowder.ncsa.illinois.edu/api/extractors/remat.experiment.from_excel
on May 9, 2025
|
|